igus igumid P150-PF carbon fiber-reinforced filament 750 g (P150-PF-0175-0750)

Highly rigid filament for structural components

igus igumid P150-PF is a professional technical filament reinforced with carbon fibers, developed for producing strong, rigid, and lightweight parts. Thanks to its flexural strength of 87 MPa and flexural modulus of approximately 4 700 MPa, it enables the printing of functional components with high mechanical stability while using material efficiently.

The filament is suitable for brackets, frames, levers, covers, mounting elements, and other structural components where low weight, rigidity, and resistance to deformation are important.

Ideal for multi-material 3D printing

igumid P150 was also developed as a structural partner for igus iglidur i150. Multi-material printing makes it possible to create a single part combining a strong load-bearing body made of P150 with sliding or friction surfaces optimized using iglidur i150 filament.

This combination is suitable, for example, for:

• structural components with integrated sliding bearings,
• lightweight handling and automation elements,
• brackets, guides, and moving mechanisms,
• functional prototypes and final technical components,
• components requiring a rigid load-bearing section and a low-friction contact surface.

High temperature resistance

Printed parts can be used continuously at temperatures up to 100 °C and for short periods at temperatures up to 125 °C. The material is therefore also suitable for technical applications where standard filaments may not provide sufficient dimensional and mechanical stability.

3D printer requirements

Carbon fibers are abrasive, so it is necessary to use a hardened or otherwise wear-resistant nozzle. A wear-resistant extruder feeding mechanism is also recommended. For reliable first-layer adhesion, an adhesive intended for igus technical filaments can be used.

The filament is suitable for FDM/FFF printers capable of processing third-party materials. To achieve reliable results, the recommendations of the printer and nozzle manufacturers must be taken into account.

Main advantages

• carbon fiber reinforcement for high strength and rigidity,
• flexural strength of 87 MPa,
• flexural modulus of approximately 4,7 GPa,
• long-term temperature resistance up to 100 °C,
• suitable for lightweight and mechanically stressed structures,
• can be used on its own or for multi-material printing,
• structural partner for iglidur i150 filament,
• black technical finish.

Notice: Due to the abrasive filler, do not use a standard brass nozzle. A hardened steel or other wear-resistant nozzle is recommended.

Key features:

• Carbon fiber reinforcement for high rigidity and strength
• Flexural strength of 87 MPa
• Flexural modulus of approximately 4,7 GPa
• Long-term temperature resistance up to 100 °C
• Suitable for lightweight structural and mechanically stressed parts
• Also designed for multi-material printing with iglidur i150
• Low moisture absorption
• Suitable for standard FDM/FFF printers with a wear-resistant nozzle