ERYONE PP CF Black 700g

ERYONE PP CF – lightweight, rigid, and chemically resistant composite

Carbon fiber reinforced polypropylene (PP‑CF) combines the low density of PP with the stiffness and strength of carbon fibers. The result is durable yet lightweight prints with lower warping tendency – excellent for industrial prototypes and functional parts.

Why choose this filament

20% carbon fiber for significantly higher stiffness and strength.
Low density (0.95–1.01 g/cm³) – lightweight parts without losing durability.
High chemical resistance and good thermal stability.
Easier to print than pure PP with proper bed preparation (PP glue recommended) and an enclosed printer.
Tensile strength up to ~50 MPa (XY) and tensile modulus ~1.3–1.7 GPa.

Recommended print settings

Nozzle: 220–240 °C
Bed: 60–80 °C
Speed: 30–100 mm/s
Environment: enclosed recommended (enclosure)
Build surface: glass / PEI / spring steel + special PP glue
Drying: usually not needed; if the filament absorbed moisture, 50–60 °C for 8 h

Tip: Carbon fibers are abrasive – for long-term printing, a hardened nozzle is recommended.

Verified mechanical and physical parameters (typical)

Property	Value
Carbon fiber content	20 %
Density	0.95–1.01 g/cm³
Tensile strength (XY)	~50.1 MPa
Tensile modulus (XY)	~1320–1675 MPa
Elongation at break (XY)	~25–32 %
Tensile strength (XZ)	~6–8 MPa
Flexural strength	~16–18 MPa
Flexural modulus	~1672–1935 MPa
Charpy impact strength	~19.1–22.3 kJ/m²
HDT (0.45 MPa)	~85 °C

Typical applications

Prototypes and parts in automotive and aerospace
Jigs, holders, covers, chemically resistant containers
Lightweight structural components, sports and outdoor accessories

Printing and compatibility notes

PP glue/release layer recommended for reliable adhesion.
CF composite is abrasive – consider a hardened nozzle for longer life.
Most FDM printers are compatible; for best results, increase first-layer temperature and minimize drafts.

Key features:

Lightweight and rigid composite: polypropylene with 20% carbon fiber
High chemical resistance, ideal for functional and industrial parts
Low density – lightweight prints without compromising strength
Stable printing with recommended PP glue and an enclosed printer
Verified mechanical parameters: tensile strength ~50 MPa (XY)
Broad use: automotive, jigs, covers, chemically resistant parts
Abrasive material – a hardened nozzle is recommended for long service life