Bambu TPU 95A HF

Bambu TPU 95A HF is an optimized TPU filament designed for high-speed 3D printing. Compared to regular TPU 95A, TPU 95A HF offers up to 3x faster print speeds, effectively solving the common issue of long print times with other TPU filaments. TPU 95A HF maintains excellent layer adhesion, impact resistance, flexibility, and low-temperature resistance, just like traditional TPU filaments. Experience fast TPU printing without compromise!

High-speed printing

Take TPU printing efficiency to the next level with Bambu TPU 95A HF, enabling prints 3× faster than standard TPU 95A.

Parameter	Bambu TPU 95A	Bambu TPU 95A HF
Nozzle temperature (°C)	230	230
Maximum volumetric flow (mm³/s)	3.6	12
Print speed (mm/s)	44	147
Model sample	Diameter: 50 mm, Height: 100 mm, Infill: 40%

Soft and flexible

Bambu TPU HF is an exceptionally soft and flexible filament with outstanding impact resistance, enabling the printing of parts that must withstand shocks, collisions, and drops.

Wide range of applications

TPU filaments are suitable for a wide variety of applications, from industrial components to protective elements and flexible parts.

Accessory compatibility

Recommended vs. Not recommended

Component	Recommended	Not recommended
Build plate	Smooth PEI plate, Textured PEI plate	Cool Plate SuperTack
Nozzle	Hardened steel nozzle (0.4 mm / 0.6 mm / 0.8 mm), Stainless steel nozzle (0.4 mm)	Hardened steel nozzle (0.2 mm), Stainless steel nozzle (0.2 mm)
Adhesive	Bambu Liquid Glue	Glue Stick

Available colors for TPU 95A HF

Color	Hex code
White	#FFFFFF
Yellow	#F3E600
Blue	#0072CE
Red	#C8102E
Gray	#898D8D
Black	#101820

Recommended print settings

•Pre-print drying: 70 °C for 8 hours (TPU 95A HF is highly moisture-sensitive – for optimal results, drying is recommended both before printing and after storage).

•Storage relative humidity: < 20% RH (in a sealed package with desiccant).

• Nozzle temperature: 220 - 240 °C

• Bed temperature (with glue): 30 - 35 °C

• Maximum print speed: < 200 mm/s

Physical properties

Property	Value
Density	1.22 g/cm³
Vicat softening temperature	N/A
Heat deflection temperature	N/A
Melting temperature	183 °C
Melt flow index	36.5 ± 2.6 g/10 min

Mechanical properties

Property	Value
Tensile strength	27.3 ± 0.8 MPa
Elongation at break	> 650 %
Flexural modulus	N/A
Flexural strength	N/A
Impact toughness	N/A

Printing tips

✔ Drying: 70 °C for 8 hours. TPU 95A HF absorbs moisture quickly, which can affect print quality. Additional drying before and after storage is recommended. See details in the filament drying guide on the WIKI.

✔ Print quality: For best results, read the TPU printing guide before starting your print.