Note: PETG HF must be dried before use to achieve optimal print quality.
We process and ship orders immediately during the business day.
PETG HF is a fully optimized PETG filament designed specifically for high-speed printing. With a default printing speed that is twice as fast as standard PETG filaments, PETG HF elevates your printing efficiency to a new level.
It effectively addresses common issues such as oozing and stringing associated with regular PETG, ensuring smoother and more reliable printing. The new matte finish not only improves aesthetics by smoothing out uneven gloss during speed transitions, but also provides a consistently uniform appearance.
Offering greater durability and toughness than PLA, PETG HF is an ideal choice for creating long-lasting objects with an enhanced surface finish and faster production.
* Adrian Luben (Social Handle: @Marsgizmo)
Twice as fast as standard PETG, PETG HF significantly boosts your productivity without compromising the quality of your prints.
Among PETG filaments, PETG HF stands out for its printability thanks to its higher adaptability to printers and print settings, achieving ideal print results without the need for fine-tuning parameters. With advanced formula optimization, PETG HF eliminates oozing and stringing, ensuring smoother prints with sharp details.
PETG HF provides a smooth texture and consistent gloss at any printing speed, ensuring uniformity and sharp details in every print.
PETG HF retains the inherent properties of regular PETG, providing excellent resistance to water, UV radiation and temperature. It is tougher and more durable than PLA, with higher heat resistance, making it an ideal choice for printing outdoor items such as flower pots, bird cages, watering cans and automotive parts. In addition, it is perfect for outdoor toys that require long-term exposure and the ability to withstand impacts, collisions and drops.
| Recommended | Not recommended | |
| Plate | Smooth PEI Plate,Textured PEI Plate | Cool Plate |
| Hotend | All Size / Material | / |
| Glue | Bambu Liquid Glue Glue Stick |
/ |
| Color | Hex Code | Display |
| Yellow | #FFD00B | |
| Orange | #F75403 | |
| Green | #00AE42 | |
| Red | #BC0900 | |
| Blue | #002E96 | |
| Black | #000000 | |
| White | #FFFFFF | |
| Gray | #ADB1B2 |
| PLA Basic |
PETG HF
|
PETG Basic | |
| Printing Speed* | ~ 300 mm/s |
~ 300 mm/s
|
~ 200 mm/s |
| Preset Printing Speed* | 258 mm/s |
258 mm/s
|
172 mm/s |
| Strength (Bending Strength - XY) | 76 MPa |
64 MPa
|
65 MPa |
| Stiffness (Bending Modulus - XY) | 2750 MPa |
2050 MPa
|
1670 MPa |
| Layer Strength (Bending Strength - Z) | 59 MPa |
48 MPa
|
48 MPa |
| Layer Adhesion (Impact Strength - Z) | 13.8 kJ/m² |
10.6 kJ/m²
|
13.6 kJ/m² |
| Toughness (Impact Strength - XY) | 26.6 kJ/m² |
31.5 kJ/m²
|
52.7 kJ/m² |
| Heat Resistance (HDT, 0.45 MPa) | 57 °C |
69 °C
|
69 °C |
1. Maximum printing speed* refers to the highest speed achievable by the filament while maintaining high printing quality, assuming an appropriate increase in nozzle temperature.
2. Preset maximum printing speed* refers to the highest speed achievable with the default settings, which ensures top print quality in most environments.
Settings: Bambu Lab X1-Carbon, 0,4 mm nozzle, 0,2 mm layer height
All printing parameters are stored in the RFID, which can be read through our AMS (Automatic Material System).
Load and print! No tedious setup.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 65 °C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 230 - 260 °C |
| Bed Temperature (with Glue) | 65 - 75 °C |
| Printing Speed | < 300 mm/s |
| Physical Properties | |
| Density | 1.28 g/cm³ |
| Vicat Softening Temperature | 70 °C |
| Heat Deflection Temperature | 69 °C |
| Melting Temperature | 214 °C |
| Melt Index | 28.2 ± 2.7 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 34 ± 4 MPa |
| Breaking Elongation Rate | 8.6 ± 1.2 % |
| Bending Modulus | 2050 ± 120 MPa |
| Bending Strength | 64 ± 3 MPa |
| Impact Strength | 31.5 ± 2.2 kJ/m² |
Dry before use for higher print quality. PETG HF must be dried before use and kept moisture-free during printing, especially for longer printing times (over 6 hours).
Drying conditions: 65℃, 8 hours in a drying oven; 75 - 85℃, 12 hours on the heated bed of the X1 series. For more information, visit: Filament drying recommendations on the WIKI.